Project: Physical Testing of Surfacing Material CTL Project No.: 102013
Contact Ted Deason CTL Project Mgr.: W. Dziedzic
Submitter: Ted Deason Technician: A.I. Saez
Approved: R.G. Burg
Date: May 6, 1991
ASTM C 779 Abrasion Resistance Test Results of Specimens
Identified as Mortex Marquee Surfacing Material “021043”
Specimens021043 / Depth of Wear
Inches
30 Minutes / 60 Minutes
A / 0.074 / 0.130
B / 0.053 / 0.097
C / 0.04 / 0.086
Average / 0.056 / 0.104
ASTM C 779 Abrasion Resistance Test Results of Specimens
Identified as Mortex Marquee Surfacing Material “011042”
Specimens021043 / Depth of Wear
Inches
30 Minutes / 60 Minutes
A / 0.051 / 0.117
B / 0.063 / 0.107
C / 0.052 / 0.090
Average / 0.055 / 0.105
* Control concrete tested was the concrete side of an abrasion specimen fabricated with the tested surfacing material on the top of a concrete base.
Test Results for ASTM C 672 Scaling Resistance of Concrete Surfaces Exposed to Deicing Chemicals of Specimen Identified as Mortex Marquee Surfacing Material “021043”
Sample Visual
Identification Cycles Rating
021043 0 0
Surfacing 5 0
Material Overlay 10 0
On Concrete* 15 0
25 2
50 3
Test Results for ASTM C 672 Scaling Resistance of Concrete Surfaces Exposed to Deicing Chemicals of Specimen Identified as Mortex Marquee Surfacing Material “011042”
Sample Visual
Identification Cycles Rating
021043 0 0
Surfacing 5 0
Material Overlay 10 0
On Concrete* 15 0
25 1
50 2
* Results are for one specimen.
Deicer Scaling Ratings:
0 no scaling
1 very slight scaling
2 slight to moderate scaling
3 moderate scaling (texture pattern not apparent)
4 moderate to severe scaling
5 severe scaling (overlay removed from surface)
Test Results for ASTM C 666 Rapid Freezing and Thawing In Water of Specimen Identified as Mortex Marquee Surfacing Material “021043”
Sample Weight Relative Dynamic
Identification Cycles Change, % Modulus, %
021043 0 0.00 100
Surfacing 46 -0.13 100
Material Only* 74 -0.26 100
109 -0.32 100
130 -0.32 99
150 -0.77 99
189 -1.32 99
229 -1.83 99
285 -2.41 99
306 -3.14 99
021043 0 0.00 100
Surfacing 46 0.13 96
Material Overlay 74 0.19 95
On Concrete 109 0.22 95
130 0.11 95
150 -0.52 98
189 -1.01 96
229 -1.23 95
285 -1.43 94
306 -1.75 93
Test Results for ASTM C 666 Rapid Freezing and Thawing In Water of Specimen Identified as Mortex Marquee Surfacing Material “011042”
Sample Weight Relative Dynamic
Identification Cycles Change, % Modulus, %
011042 0 0.00 100
Surfacing 46 -0.13 100
Material Only* 74 -0.10 100
109 -0.16 100
130 -0.16 99
150 -0.78 99
189 -1.50 99
229 -1.96 99
285 -2.55 99
306 -3.43 99
011042 0 0.00 100
Surfacing 46 0.04 95
Material Overlay 74 0.09 93
On Concrete 109 0.08 93
130 0.08 93
150 -0.45 94
189 -0.69 91
229 -1.13 87
285 -1.38 83
306 -1.69 77
*Results are for one specimen.
* *Results are an average of four specimens.
Test Results for ASTM C 666 Rapid Freezing and Thawing In Water of Specimen Identified as Mortex Marquee Surfacing Material “021043”
Material / Compressive Strength, psi021043
2 - inch cubes (ASTM C 109) / 3 days / 7 days / 14 days / 28 days
2110 / 2780 / 3760 / 4560
Test Results for ASTM C 666 Rapid Freezing and Thawing In Water of Specimen Identified as Mortex Marquee Surfacing Material “011042”
Material / Compressive Strength, psi011042
2 - inch cubes (ASTM C 109) / 3 days / 7 days / 14 days / 28 days
1970 / 2680 / 3420 / 4290
Notes: All test results are an average of three specimens. Specimens cured
in lime-saturated water at 73±3°F until removed for test.
Mortex Manufacturing Co., Inc.
1818 W. Price Street
Tucson, AZ 85705 USA
520-887-2631 www.mortex.com