MAT_SCI 360

Introduction to Electron Microscopy

Fall 2016

TEM Laboratory 1:

Introduction to TEM, Basic TEM operation and Electron Diffraction

Introduction

This laboratory is designed to introduce one of the basic transmission electron microscopes: Hitachi H-8100 Transmission Electron Microscope. In this initial laboratory, the methods for basic operation and alignment of the instrument will be covered. You will also observe methods for sample preparation (covered in the first Introduction and Safety Tour). The purpose of this lab is to get you familiar with the standard operation of the TEM and general facility practices.

As you know from the course lectures, TEM is to generate and analyze transmitted electrons scattered by electron-specimen interactions. Electrons scattered to different angles may contribute to different contrasts in imaging. For this first laboratory, we will only be collecting imaging showing mass-thickness contrast and diffraction contrast.

Learning Objectives: By the end of this laboratory session, you should be able to:

  1. Understand how to prepare TEM samples of nano-materials.
  2. Load TEM grids onto the sample holder; and Insert/Take out the holder into the H-8100 TEM.
  3. Adjust Gun-Tilt, Gun-Shift, Condenser Lens Aperture and Condenser Lens Astigmatism to get a well-aligned electron beam.
  4. Set up Eucentric height, Adjust the Beam-Tilt and Objective lens Astigmatism to get a high quality TEM image.
  5. Do basic selected-area electron diffraction, by using the selected-area aperture.
  6. Do basic bright-field imaging by put in objective aperture and select the transmitted beam.
  7. Do basic dark-field imaging by put in objective aperture and select the diffracted beams.

Lab Background: Review of some basic principals you learnt from the class:

1.Electron source: There are two kinds of commonly used electron sources 1) Thermionic electron gun by using W and LaB6 as the filament and 2) Field emission gun (single crystal W).

2.Brightness: electron beam brightness is defined by electron current measured within an unit area and unit solid angle. The figure below shoes the relationship between emission current/brightness vs Bias voltage:

3.Defects of a magnetic lenses: spherical aberration refers to lens imperfections lead to different focal lengths in center and at edges of lens

4.Defects of a magnetic lenses: astigmatism refers to lens defect caused by magnetic field asymmetry.

5.Chromatic Aberration: additional blurring due to energy spread in electron beam and lens current fluctuations.

6.Deflection coils: provide means to shift or to tilt the electron beam. It can be applied to correct mechanical misalignments of the optical system, or to obtain specific imaging effects. It can be applied as Gun Coils, Beam Coils, Image Coils and Scanning Coil etc.

7.Interaction of high energy electron with specimen is a complicated process. Signals generated in such interactions include secondary electron (SE), backscattered electron, X-rays, Auger electrons, visible light, transmitted electron, transmitted and elastically scatted electron and transmitted and inelastically scatted electron.

8.While image is formed in the focal plane of the objective lens, electron diffraction can be obtained from the back-focal plan of the objective lens. Electron diffraction can be applied to study crystalline structures. You need some basic crystallography knowledge to interpret the electron diffraction patterns (more will be covered in the second TEM lab).

Laboratory procedures:

  1. Basic safety issues
  • Emergency evacuation
  • Chemical contamination
  • Electric shock
  • Other safety issues: read departmental safety plan, EPIC facility rules and TEM lab safety draft. Sign the safety training sheet.
  1. Login/reserve/logout FOM system

Visit from any internet connected computer

Use mse360 as user ID, account number and password

  1. Sample preparation equipments (Contact Drs. Jinsong Wu and Kai He at EPIC when you need help on TEM sample preparation)
  2. Cutting: wheel saw, wire saw, ultrasonic cutters…
  3. Polishing: mechanical polishing, electro-chemical polishing…
  4. Dimpling: Gatan dimple grinder
  5. Ion milling: PIPS, IBT
  6. Microtome
  1. Basic TEM operations (Please download H8100 TEM operation manual from bring it with you for all TEM labs)

Microscope startup

Obtaining good electron illumination

Setting the sample at eucentric height

Condenser lens alignment

Beam tilt purity (compensation)

Objective lens alignment (Voltage center)

Image focus and astigmatism correction (Fresnel-fringe method)

TEM shutdown

5. Selected area (SA) electron diffraction

  • Find and center an interesting area
  • Insert and center a suitable SA aperture
  • SA aperture is focused in SA mode
  • Press Diff.
  • Form a parallel illumination on the sample by turning Brightness counterclockwise.
  • Focus the pattern by adjusting intermediate lens current I1 to
  • Record a few SA diffraction pattern with different exposure time.
  • If CCD camera is used, make sure that the CCD camera is not saturated. Tip: Start with very short exposure time and use beam stopper. (When CCD camera is saturated, there is a streaking across the direct spot).

Laboratory Report:

In your laboratory report you should provide a description of all micrographs taken and concise discussion of differences you see. The handouts and your textbook should be sufficient for you to interpret your results, but you should provide an explanation in your own words. It is recommended to section your report into different sections including Introduction, Experimental, Results, Discussion etc.

In your Experimental section, you will need to

1). Acquire a normal TEM image of the Au nanoparticles;

2). Acquire a bright-field TEM image of the Au Nanoparticles;

3). Acquire a dark-filed TEM image of the Au nanoparticles;

4). Acquire a selected area diffraction pattern from Au particles and index the diffraction rings (write down necessary TEM parameters).

H8100 Daily Operation Guide

Last modified on June 2016 by Dr. Jinsong Wu

Note: This guide is NOT complete operation manual of H8100. It is only for your daily operation quick reference. For detailed operation manual, please refer to

Remember:

  1. Please send a copy of your publication (e-format preferred) to Jinsong () if you use any TEM results taken with this microscope! We highly appreciate if you include NUANCE Center in the Acknowledgement.
  2. Adjust the alignment settings ONLY when necessary.
  3. Refill Liquid Nitrogen if your experiment goes over 2 hours.

BEFORE YOU START

  • Check conditions of H8100 before login the access control. (Turn on Panel Lamp at right side of control panel if necessary)
  • Vacuum lights (Gun=green, column=green, specimen=yellow, camera=green);
  • Sample position (X=0, Y=0, tilt=0), Apertures position (Condenser=1, Objective=0, Selected area=0);
  • Filament=OFF, HV=200 (CRT), probesize=micro3, Zoom (left panel) &Bright (right panel) ON.
  • Check FOM records to see notes left by previous user.

START-UP

  1. Fill LN2, Log in Access Control in FOM,
  2. If you need to Turn off HV, pressAcc. VoltageReady/OFF twice; Load Specimen. Remember to check the O-ring!
  3. If you need to Turn on HV, pressAcc. VoltageReady/OFFonce, press 200KV to increase HV.
  4. Apply Filament Current SLOWLY (20 seconds per division). Stop at one division before maximum.

FIND BEAM

  1. Check emission current (HV/BEAM meter, 0<current < 10 A.).
  2. Follow these steps to find the beam. Skip to next part (step 7) whenever you see the beam.
  3. Dim or turn off room light. Remove cover of viewing chamber. Decrease MAGNIFICATION to see if beam appears. If yes, go to next part (step 7).
  4. Press LOW MAG. If you see the beam, move a hole on your specimen to the center of the screen. Focus the beam to small spot through the hole on the sample; go back to ZOOM mode (press ZOOM). Adjust sample position and BRIGHTNESS to find the beam.
  5. Call for help if you still cannot find the beam.

CHECK Gun Tilt

  1. Change MAG to 20K. Adjust BRIGHTNESS to get the smallest beam spot.
  2. Center beam with BRIGHTNESS CENTERING. It should look like fig. 1a or 1b.
  3. Adjust GUN TILT slowly and see the feature change. Try to find the brightest and the most symmetrical position of the beam (fig.1a).(Do not touch GUN HORIZ knob at this step!)
  4. Slowly increase Filament current until you see saturated beam as shown in fig. 1c.

CHECK GunHORIZ (To remember the knobs used in this step, “1C-4G”)

  1. Change MAG=8K. Make sure Probe Size on CRT is 3, center beam with BRIGHTNESS CENTERING.
  2. Use SPOT SIZE knob (left sub panel) to select probe size 1, center beam with BRIGHTNESS CENTERING.
  3. Select probe size 5, center beam with Gun Horiz.
  4. Repeat last two steps until beam is centered at both probe 1 and 5.
  5. Set probe size back 3 when finish alignment.
  6. Center beam with BRIGHTNESS CENTERING.

CHECK Condenser lens (C2) Aperture centering

  1. Change BRIGHTNESS largely back and forth to see how the beam image changes.
  2. If the beam spread and shrink uniformly like fig 2a, go to Find specimen part (step 23).
  3. If it changes from fig. 2b to fig. 2c with changing brightness: a). Focus the

bean to the cross-over, center it by using BRIGHTNESS CENTERING.

b). Spread the beam out by turning BRIGHTNESS knob clockwise;

c). adjust C2 position knobs on the aperture handler to center the beam.

CHECK Condenser lens stigmatism

  1. Change BRIGHTNESS largely back and forth to see how the beam image changes.
  2. If the beam spread and shrink uniformly like fig 3a, Skip to next part (step 23).
  3. If it changes from fig. 3b to fig. 3c with changing brightness, adjust COND STIG until it spread and shrink uniformly as shown in fig. 3a.

FINDspecimen and SET eucentric height

  1. Change MAG>=8K. Move specimen to find a small feature with sharp edge.
  2. Check OBJ current on the CRT and set it to 5.25 (adjust FOCUS or press reset under the CRT)
  3. Spread beam with BRIGHTNESS to cover whole screen, as long as you can still see specimen image.
  4. Turn on Wobbler (right panel) and the feature may vibrate.
  5. Adjust Thumb-screw on goniometerto minimize the vibration.
  6. Turn off Wobbler when you finish.

VoltageCenter Alignment

  1. Move specimen to find a very small feature with sharp edge on your specimen under MAG=10-25K. Decrease or increase MAGNIFICATION if necessary. Use binocular if necessary.
  2. Spread beam with BRIGHTNESS to cover whole screen.
  3. Turn on CCD Camera (in Search Mode): refer to CCD instructions.
  4. Under CRT (left), make sure STOP button is lit on. Press PHOTO to raise viewing screen.
  5. Center the small feature to the center of CCD with Specimen transition knobs
  6. Turn on HV Modulation (right panel). The image feature may vibrate. (Spread beam if you see beam vibrating other than image feature.)
  7. Adjust Beam Tilt (right sub panel) to minimize the vibration of the feature.
  8. Repeat last step at Mag 100k or higher if lattice imaging is needed.
  9. Turn off HV Modulation.

Objective lens stigmatism

  1. Find and center a amorphous area in the CCD, under Process menu click Live and then Reduced FFT;

Turn FOCUS knob (right panel) and watch for the inner circle in the FFT window; use OBJ STIG X&Y knobs (left sub panel) to make the inner circle as round as possible (increase time to 0.9 s, if contrast of the ring is low). Tips: dark fringe (over focus), bright fringe (underfocus).

  1. Turn FOCUS knob to maximize the diameter of the inner circle in the FFT window. Now we are closed to the optimal focus value. Fine tune can be done by looking at the image carefully.

Take Picture

  1. Always take picture with underfocus (white edge).
  2. To take picture with digital CCD imaging, follow separate manual.
  3. To take picture with negatives, change exposure time (left of CRT) to AUTO and check exposure time on CRT. Typical time is less than 5 seconds. Make sure that the STOP light underCRT is not lit. Press FEED and then PHOTO to take pictures.

Selected Area Diffraction (Skip if you don’t need SAED analysis)

  1. Find and center an interesting specimen area
  2. Insert and center a suitable SA aperture
  3. Press SA (left panel)
  4. Make sure that the * is at left corner of intermediate lens current I1 on the TEM monitor. If not, click up/down arrow key to cancel any highlighted item on the TEM monitor. Input 5 from keyboard (left panel) and press return. Focus SA aperture using DIFFRACTION SPOT knob (left panel) and binocular.
  5. Make sure that the STOP light on TEM data monitor is lit. If no, press STOP once to make it lit.
  6. Press Diff (left panel). If the central spot is not at the viewing center, center it using the INTER ALIGN X and Y knobs (left sub panel). If the spot is not round, make it round using INTER STIG X and Y knobs.
  7. Spread beam by turning Brightness counterclockwise. Diffraction spots will become weaker and smaller.
  8. Focus the pattern by adjusting DIFFRACTION SPOT (left panel).
  9. Record a few SA diffraction patterns the CCD. Please use the beam stop if the transmitted spot is too bright!!

Bright Field/Dark Field Imaging (Skip if you don’t need Dark Field imaging)

  1. Follow previous step, insert and center a suitable Objective aperture on Transmitted spot of SAED pattern.
  2. Press ZOOM, remove SA aperture to see Bright Field image. Adjust focus and/or obj stigmatism if necessary.
  3. Check exposure time and take image (see step 41).
  4. Remove Obj aperture, insert SA aperture and press DIFF to go back to SAED mode. Center Obj aperture to one diffractio spot.
  5. Repeat 52&53 to record Dark Field image. You may set manual exposure time if image is too dark.

TEM shutdown

  1. Turn MAG down to 8000, center beam and spread beam to cover whole screen.
  2. Move specimen to origin: X=0, Y=0, Tilt=0
  3. Turn MAG to 6K
  4. Slowly turn the Filament current to off (3 minutes)
  5. PressAcc. Voltage READY/OFF twice to switch HV off
  6. Check or set these settings to standby mode:

● OBJ aperture OUT● SA aperture OUT● Condenser aperture=1

  1. Make sure specimen position at origin, take specimen holder out of the column
  2. Remove specimen and insert specimen holder back to TEM till STOPposition. Push EVAC switch to evacuate.