W8411SLMMDF (CLEAR) BASE (FOR MDF/PB)

/ Office: 118 Nguyen Phi Khanh St, Tan Dinh Ward, District 1, Ho Chi Minh City, Vietnam.
Tel: (848) 3 820 6932 Fax: (848) 3 820 2055
Email: Website:
Factory: Lot A-3A-CN, My Phuoc 3 Industrial Zone, Ben Cat, BinhDuongProvince.

PRODUCT INTRODUCTION

Description Rapid Single Component

Water-base Modified Polysiloxane Sanding Sealer.

Uses Furniture, Flooring and

Paneling made from timber and

MDF substrates.

Application Spray

COATING PERFORMANCE

  • Self cross-linking, rapid curing
  • Excellent sandability
  • Outstanding water resistance
  • Excellent adhesion on timber substrates
  • Excellent resistance to UV irradiation
  • Excellent stain resistance
  • Excellent dirt pick-up resistance
  • Outstanding ability to high-light wood-grain pattern (for transparent coating)
  • Excellent fungus resistance
  • High built
  • Outstanding close-pore finish for MDF

PHYSICAL AND CHEMICAL PROPERTIES

Specific Gravity

(27 oC)1.52 – 1.58

Solid Content (%)28 – 32

Viscosity ( 27 oC)25 – 31 sec F#4 Cup

Binder TypeModified Polysiloxane

PRODUCT PREPARATION

Mixing RatioW8411SLMMDF Base

100 parts by weight

Reducer 0 to 30 parts by weight

ReducerW8046R Reducer

APPLICATION PARAMETER

Theoretical Coverage

(m2/L)10 – 16 (subject to substrate porosity).

Coating System2 coats of W8411SLM MDF Base, sanded, followed by 2 to 3 coats of MDF White or coloured basecoat, then followed by 2-3 coats of Gloss or Satin (clear).

Application temperature10 oC - 50 oC

Touch-dry Time (27 oC)10 – 15 minutes

Hard-dry Time (at 27oC)About 30 minutes.

GENERAL PROPERTIES

W8411SLM MDF Base is a water-based rapid single component ModifiedPolysiloxane Sanding Sealer formulated specially for application on timber substrate via spray application. This product is designed for self cross-linking to provide a rapid curing, hard and durable coating for MDF substrate with excellent adhesion property, scrub, UV, stain, water, fungus and dirt pick-up resistances. This product being water-based, is non-flammable.

SHELF LIFE

12 months from date of manufacture. The date refers to product held in its original closed packaging.

STORAGE

Keep containers in a cool ventilated environment, temperature between 5 oC to 40 oC. With partial use, close container tight and use the remainder as soon as possible.

/ Office: 118 Nguyen Phi Khanh St, Tan Dinh Ward, District 1, Ho Chi Minh City, Vietnam.
Tel: (848) 3 820 6932 Fax: (848) 3 820 2055
Email: Website:
Factory: Lot A-3A-CN, My Phuoc 3 Industrial Zone, Ben Cat, BinhDuongProvince.

W8411SLM MDF (CLEAR) BASE

Advance water-based wood lacquer

Biochem International J.S. Company

Office: 118 Nguyen Phi Khanh, Tan Dinh Ward, Dist.1

Tel: (84-8) 3 8206 932 / 3 8207 927 Fax: (84-4) 3 820 2055

Email: Website:

Technical Data Sheets (TDS)October 2009

Advance Water-based Wood LacquerPage:1

Biochem International J.S. Company

Office: 118 Nguyen Phi Khanh, Tan Dinh Ward, Dist.1

Tel: (84-8) 3 8206 932 / 3 8207 927 Fax: (84-4) 3 820 2055

Email: Website:

FILM PROPERTIES

Property / Results
Touch-dry / 10-15 minutes
Hard-dry / About 30 minutes
Adhesion / 100 mm2. No Detachment.
Flexibility / 2mmMandrel.
Impact / 45cm
Hardness / 1 – 2H (Without Part B)
Hardness / 2 – 3H (With Part B)

CONTROLLED MATERIALS IN

WET PAINT

Harmful Chemicals / *Level
Aromatic Hydrocarbon / 0 mg/kg
Halogenated Compound / 0 mg/kg
Formaldehyde / < 0.02%
Mercury / 0 mg/kg
Lead / 0 mg/kg
Cadmium / 0 mg/kg
Chromium / 0 mg/kg
Total Volatile Organic Content (TVOC) /  150 g/L

* These chemicals are not used in the manufacture of our product. However, minute traces may be present due to environmental contamination beyond our control.

COMMENT

Tests were performed on paint films applied at 100 wet film and allowed to cure at 27 2oC for 7 days. Relative Humidity was maintained at 80% during the period of film curing.

The information in this brochure has been compiled in accordance to our best knowledge at the date of

issue and is based on recent technological and scientific developments.

However, this information should not be construed into recommending the use of our product in violation of any patent or as warranties (express or implied) of non-infringement or its fitness for any particular purpose.

Prospective purchasers are invited to conduct their own tests and studies to determine the fitness Biochem products for their particular purposes and specific applications.

Due to the varying techniques and conditions applied, Biochem accepts no responsibility for any use of the product, may be by way of experiment or manufacture nor does Biochem accepts any responsibility for the used techniques in any application whatsoever. Biochem does not warrant against infringement of patents of third parties by reason of any uses purchasers make of the product.